Insulating Silica Fire Brick For Glass Kiln , Acid Resistance
Refractory Fire Bricks
Silica brick is SiO2 content of not less than 96% of the silica as
raw materials, adding mineralants (such as scales, lime milk) and
binding agent (such as sulfite pulp waste) by mixing, molding,
drying, firing and other processes be made of. The higher the SiO2
content in the silica raw material, the higher the refractoriness.
Impurity components K2O, Na2O, etc. are harmful, will seriously
reduce the refractory products refractory. Fe2O3, CaO, MgO and
other impurities from the role of flux. Advanced silicon brick raw
materials subject to special treatment, remove impurities.
1.Good acid and erosion resistance, powerful anti high-temperature
2.Soften melting temperature is 1620~1670 °C.
3.Low Thermal shock resistance.
4.Natural silica as raw material, plus regular mineralizer.
5.Ensure good bonding and structural strength of furnace.
6.Good heat resistance and long service life
1.Glass melting furnace, ceramic frit kiln, sodium silicate
furnace, soaking furnace, ceramic kiln, etc
2.Coke oven’s coking chamber, combustion chamber walls, steel
open-hearth ‘s regenerator and sediment chamber, etc.
3.Load-bearing parts of high temperature hot air furnace and acid
open-hearth furnace roof, etc.
Specification of Silica Brick:
|Item:||Stella HD||Stella HD|
|Apparent Porosity: %||≤22||≤24|
|True Density: g/cm3||2.34||2.35|
|Cold Crushing Strength: MPa||≥60||≥40|
|Refractoriness Under Load (0.2MPa): ℃||≥1660||≥1660|
|Residual Quartz: %||≤1.0||≤1.0|
|Creep Rate 0.2MPa ((1550℃*50h): %||≤0.8||≤0.8|
|Reheat Linear Change ( 1450℃*2h):%||≤0.2||≤0.2|
|Heat Expansion Coefficient (1000℃) %||≤1.26||≤1.26|